Uniformity of electron beam cross-linking of polyethylene depending on the distribution of the absorbed radiation dose

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Рұқсат ақылы немесе тек жазылушылар үшін

Аннотация

The crosslinking of polyethylene of pipe grades via 900 keV electrons at an absorbed dose of 50 to 400 kGy in the presence of antioxidants and a crosslinking agent was studied. The degree of crosslinking of polyethylene was measured by the content of the gel fraction, determined by its extraction in xylene. It was shown that in all cases the 60% degree of cross-linking is achieved at a dose of about 100 kGy. It is advisable to combine the standard method for determining the gel fraction with visual inspection of samples to identify the conditions for the formation of an excessively low-melting material. It has been shown that ±7% crosslinking degree non-uniformity can be achieved with dose non-uniformity of up to ±50%.

Толық мәтін

Рұқсат жабық

Авторлар туралы

A. Popova

Frumkin Institute of Physical Chemistry and Electrochemistry RAS

Email: ponomarev@ipc.rssi.ru
Ресей, Moscow

K. Artamonova

Frumkin Institute of Physical Chemistry and Electrochemistry RAS

Email: ponomarev@ipc.rssi.ru
Ресей, Moscow

A. Bludenko

Frumkin Institute of Physical Chemistry and Electrochemistry RAS

Email: ponomarev@ipc.rssi.ru
Ресей, Moscow

E. Kholodkova

Frumkin Institute of Physical Chemistry and Electrochemistry RAS

Email: ponomarev@ipc.rssi.ru
Ресей, Moscow

S. Vlasov

Frumkin Institute of Physical Chemistry and Electrochemistry RAS

Email: ponomarev@ipc.rssi.ru
Ресей, Moscow

A. Ponomarev

Frumkin Institute of Physical Chemistry and Electrochemistry RAS

Хат алмасуға жауапты Автор.
Email: ponomarev@ipc.rssi.ru
Ресей, Moscow

Әдебиет тізімі

  1. Burillo G., Clough R.L., Czvikovszky T., Guven O., Le Moel A., Liu W., Singh A., Yang J., Zaharescu T. // Radiat. Phys. Chem. 2002. V. 64. P. 41.
  2. Dorigato A. // Adv. Ind. Eng. Polym. Res. 2021. V. 4. P. 53.
  3. Geyer R., Jambeck J.R., Law K.L. // Sci. Adv. 2017. V. 3. P. e1700782.
  4. Chmielewski A.G. // Radiat. Phys. Chem., 2023. V. 213. P. 111233.
  5. Ponomarev A.V., Gohs U., Ratnam C.T., Horak C. // Radiat. Phys. Chem. 2022. V. 201. P. 110397.
  6. Ponomarev A.V. // High Energy Chem. 2020. V. 54. P. 194.
  7. Woods R., Pikaev A. // Applied Radiation Chemistry. Radiation Processing. NY: Wiley, 1994.
  8. Pikaev A.K. // High Energy Chem. 2000. V. 34.
  9. Ponomarev A.V. // Radiat. Phys. Chem. 2016. V. 118. P. 138.
  10. Albrecht V., Simon F., Reinsch E., Schünemann R., Gohs U., Kretzschmar B., Peuker U.A. // Recover. Recycl. Technol. Worldw. 2016. V. 2. P. 36.
  11. Cleland M., Galloway R., Genin F., Lindholm M. // Radiat. Phys. Chem. 2002. V. 63. P. 729.
  12. Perrin C., Griseri V., Laurent C. // IEEE Trans. Dielectr. Electr. Insul. 2008. V. 15. P. 958.

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig. 1. Dependence of the degree of crosslinking of polyethylene on the dose in the presence of A1 and CA.

Жүктеу (488KB)
Метадеректер
3. Fig. 2. PE-4 samples after boiling in xylene depending on the dose D (kGy) and additives: A1 (a) and A2 (b).

Жүктеу (1MB)
Метадеректер
4. Fig. 3. Dependence of the degree of crosslinking of polyethylene on the dose in the presence of A1. Fig.

Жүктеу (481KB)
Метадеректер
5. Fif. 4. Dependence of the degree of crosslinking of polyethylene on the dose in the presence of A2 and CA.

Жүктеу (995KB)
Метадеректер
6. Рис. 5. Зависимость степени сшивки полиэтилена от дозы в присутствии А2.

Жүктеу (1022KB)
Метадеректер

© Russian Academy of Sciences, 2025